Lead Free FloSafe & Envirosafe®

64

FLOSAFE™

DESCRIPTION

97% Tin/3% Copper is alloyed from pure virgin metals and contains tin, and copper. It is economical to use when lead-free solder is required and meets all State and Federal Specifications for potable water applications.

APPLICATIONS

Sealing, joining, coating and filling of all solderable metals.  Used in plumbing, heating and industrial applications. The solder to use on brass, bronze, copper, galvanized iron, monel, steel, stainless steel and all other solderable alloys that require maximum reliability of solder joints.

FLUXES

For steel and copper use Canfield’s SOLDER-MATE Liquid Soldering Flux.  For copper pipe use COPPER-MATE Self-Cleaning Soldering Paste Flux or AQUA-BRITE Water Soluble Flux.  On stainless steel use SIL-CAN Liquid Soldering Flux. 

  • TEMPERATURE RANGE:  440 - 590° F (room temperature)
  • SHEAR STRENGTH: 6,500 PSI (room temperature)
  • TENSILE STRENGTH: 5,500 PSI (room temperature)
  • DENSITY:  .264 pounds per cubic inch
  • ELECTRICAL CONDUCTIVITY: 8.5 Sm/mm2

PACKAGING AND STORAGE INFORMATION 

Available in bar, solid wire, cored wire.  Fine wire sizes are also available. Please call for your specific needs.  

ENVIRO-SAFE®

LEAD-FREE SILVER BEARING ALLOY 

DESCRIPTION

ENVIRO-SAFE® was developed to meet the lead-free requirements of the automotive, industrial, electronic and electrical industries.

This product is excellent when the requirements for a minimum melting temperature, combined with a small melting range and excellent capillary action, is desirable. 

ENVIRO-SAFE®, a tin, silver, copper enhanced alloy is LEAD-FREE and NON-TOXIC. Contains tin, copper, and silver.

It is alloyed from ASTM Grade A tin, pure silver and copper, which gives this product its excellent properties.

PHYSICAL PROPERTIES

  • MELTING RANGE: 419 - 443° F
  • TENSILE STRENGTH8,000 psi 

PACKAGING AND STORAGE INFORMATION

ENVIRO-SAFE® is available in solid wire, cored wire, bar, ribbon, paste and preforms. Please call for your specific needs.